以电解铝硅钛合金为基 ,在工厂的生产条件下熔炼成与 ZL10 8合金成份基本相同的铸造 AST10 8铝合金 ;对比分析研究了 AST10 8和 ZL10 8合金的疲劳性能 .结果表明 ,AST10 8合金比 ZL10 8合金具有更长的疲劳寿命 ,其主要原因是由于 AST10 8合金中自然存在的钛元素细化了 α(A1)晶粒 ,也使共晶硅粒子分布更加均匀 .用扫描电镜对疲劳断口观察后发现 ,疲劳裂纹都萌生于试样表面或亚表面的氧化物夹杂等缺陷处 ,减少夹杂等铸造缺陷对提高铸造铝合金的疲劳性能有利 .
Abstract：Aluminum casting alloy AST108 is based on electrolyzing aluminum silicon titanium master alloy, and it is melted under real production conditions. The compositions of the alloy accord with that of ZL108 alloy. Fatigue properties of the alloy is investigated and compared with that of ZL108 aluminum casting alloy. The results show that fatigue life of AST108 alloy is longer than that of ZL108 alloy. The main reason is that AST108 alloy contains naturally titanium element making α (A1) dendrite cell size of the alloy small and also increasing evenness of eutectic silicon particle distribution. The fatigue fracture surface of the alloys was surveyed by means of a scanning electron microscope. It can be seen that fatigue crack originates from oxide inclusion or casting defects that is on the surface or sub surface of tested specimens. So, lessening oxide inclusion and casting defects can lengthen fatigue life of aluminum casting alloy.
[1] 杨冠群 ,顾松青 ,刘高兴 ,等 .铝矿处理并直接电解生产铝硅钛合金 (1) [J].有色金属 ,1993,(6 ) :19～ 2 3.
[2 ] 杨冠群 ,顾松青 ,刘高兴 ,等 .铝矿处理并直接电解生产铝硅钛合金 (2 ) -除铁矿粉电解生产铝硅钛合金 [J].有色金属 ,1994,(2 ) :11～ 15 .
[3] 杨冠群 ,顾松青 ,刘高兴 ,等 .直接电解生产铝硅钛合金试验结果概述 [J].铝镁通讯 ,1993,(1) :32～ 38.
[4] 杨冠群 ,顾松青 ,刘高兴 ,等 .铝矿处理并直接电解生产硅钛合金 (3) -铝硅钛合金的应用 [J].有色金属 ,1994,(3) :8～ 10 .
[5 ] 匡震帮 ,顾海澄 ,李中华 ,等 .材料的力学行为 [M].北京 :高等教育出版社 ,1998.2 0 7～ 2 18.
[6 ] 浙江大学数学系高等数学教研组编 .概率论与数理统计 [M].北京 :人民教育出版社 ,1979,2 44～ 2 46 ;34 1.
[7] 王中光译 .材料的疲劳 [M].北京 :国防工业出版社 ,1993.2 12～ 2 16
基本信息:
中图分类号:TG113.25
引用信息:
[1]王明星,翁永刚,刘志勇,王雪青,程桂萍.铝硅钛合金的疲劳性能[J].郑州大学学报(自然科学版),2000(03):32-35.
基金信息:
河南省科技攻关项目
2000-09-20
2000-09-20